3D-POWDER SLS NYLON11 15-85, fine & narrow particle size distribution polyamide 11 (Nylon 11) powder for high resolution SLS printing

• ideal SLS powder for direct SLS printing of high quality Nylon 11 parts
  
• white thermoplastic SLS powder with very high toughness and mechanical strength
  
• printable by most plastic / polymer powder SLS printers
• similar properties and printing settings to Formlabs Nylon 11, EOS PA 1101, and Rolaserit PA11 (AM Polymers) 
• bio-based
• excellent flow and levelling
• typical narrow particle size distribution in microns (not to be considered a specification):
  
  • D100: 140 (100% of particles have less than 140 microns)
  • D90: 85  (90% of particles have less than 85 microns)
  • D50: 43 (50% of particles have less than 43 microns)
  • D10: 15 (10% of particles have less than 15 microns)
  • D1: 3 (1% of particles have less than 3 microns)
• high accuracy and resolution up to 50-100 microns of final products (depending on laser spot size and layer thickness)

Typical Properties*:

• Shore hardness D75-80
• density: 1.04 g/cm³
• water Absorption after 24 hours: <1 %
• tensile strength: 45-50 MPa
• tensile modulus:  1700-1900 MPa
• elongation at break: 40-50 %
• Izod impact Strength Notched: 100 J/m
• flexural strength: 45-50 MPa
• flexural modulus 1200
• Vicat softening temperature: 175-185ºC
• melting temperature: 180-190ºC
• Coefficient of Friction COF: 0.3
• Heat Deflection Temperature HDT at 1.8MPa: 45-50ºC
  
• service temperature from -40ºC up to 100ºC (continuous) / +150ºC (short term)

Recommendations for SLS printing of Nylon 11:

• recommended plastic or polymer powder SLS printers: SLS printer compatibility
  • suitable for FORMIGA P 110 Velocis, EOS P 396, and EOS P 770
• recommended printing process: use the std printing parameters of your equivalent polymer powder and follow 3Dresyns IFU for SLS printing

Recommendations for Cold Fusion SLS printing of Metals, Ceramics, and exotic powders by Cold Metal Fusion (CMF) , Cold Ceramic Fusion (CCF), Cold Polymer Fusion (CPF), and Cold Exotic Powder Materials Fusion:

• Add 10% of 3D-POWDER SLS NYLON11 15-85 for improved and faster debinding. For more info read:
  • About Cold Metal Fusion CMF, Cold Ceramic Fusion CCF, and Cold Exotic Powders Fusion CEPF
    
  • Powder Binders for SLS Cold Metal, Ceramic & Exotic Powder Fusion

*Note: the reported properties may vary depending of part design and manufacturing practices. It is the manufacturer’s responsibility to adjust the printing parameters and validate the suitability of the printed parts for the intended use. 3Dresyns. makes no guarantee of properties, expressed or implied, regarding the accuracy of these results to be obtained from the use thereof. Standards: Shore hardness (ISO868), density (ISO 1183), water Absorption after 24 hours (ISO 62), tensile strength (ISO 527-2), tensile modulus (ISO 527-2), elongation at break (ISO 527-2), Izod impact Strength Notched (ASTM D256 & ISO 180), flexural strength (ISO 178), flexural modulus (ISO 178), Vicat softening temperature (ISO 306/B50), melting temperature (ISO 11357), Coefficient of Friction COF-Static (ISO 8295), Heat Deflection Temperature HDT (ISO 75)