3Dresyn SAE1 has these features and benefits:
- recommended for printing water and alcohol swellable absorbent hydrogel 3D materials
- ideal for making soft gels or jellies / elastic hydrogel materials with Shore O30, which cannot be directly 3D printed due to their excessive softness and resilience
- ideal for intricate, complex and highly customizable scaffold structures that can support cell adhesion and promote cell infiltration for tissue engineering 3D and for printing hydrogel scaffolds
- absorbs more than 2-3 times its weight of water and/or alcohol without losing its original shape
- ideal resin for designing high dielectric permittivity elastomers since admits water (permittivity of water is εr =80 at 20ºC and 1kHz)
- elastic with elongation >>200 % after overnight dipping in water and/or alcohol
- medium hard, soft and flexible before dipping
- Shore Hardness A20 before dipping / O30 after dipping
- Tensile strength <2 MPa before dipping / <0.2 MPa after dipping
- Flexural strength <2 MPa before dipping / <0.2 MPa after dipping
- soft and elastic (Young modulus <2 MPa before dipping / <0.2 MPa after dipping
- fast swelling in water and alcohol
- tack free finishes after light box postcuring
- flexible material that swells and becomes very soft while keeping its original shape
- elongation >100% before dipping / >>200% after dipping
- very low viscosity, below 20 cps
- high resolution
- printable by most commercial and professional SLA, DLP & LCD 3D printers
- fast printability with even low power LCD printers
- increased durability of the resin tank
- metal and organo-tin free
- it can be combined as you wish with 3Dresyn NS1 for choosing your optimum final consistency after dipping
- clear color. Choose and add your own color: 3Dresyns colors
- clean and postcure your 3D prints with Cleaning Fluid WS1 Bio
After placing your order request the Instructions for Use "IFU" at: