3D-POWDER SLS HDPE35-65, fine & narrow particle size High Density PolyEthylene HDPE powder for high resolution SLS printing

• • low coefficient of friction, abrasion/wear resistance, high impact strength, chemical and corrosion resistance, self-lubrication characteristics, zero moisture absorption, cryogenic capability, electrical resistivity
• translucent thermoplastic SLS powder with high low temperature toughness
  
• printable by most plastic / polymer powder SLS printers
• excellent flow and levelling
• typical narrow particle size distribution in microns (not to be considered a specification):
  • D100: 90 (100% of particles have less than 90 microns)
  • D90: 65 (90% of particles have less than 65 microns)
  • D50: 50 (50% of particles have less than 50 microns)
  • D10: 35 (10% of particles have less than 35 microns)
  • D1: 3 (1% of particles have less than 35 microns)

• ultra high accuracy and resolution up to 50-100 microns of final products (depending on laser spot size and layer thickness)
  
• compliant with FDA and USDA for use in food processing and medical
  applications

Typical Properties*:

• Shore hardness D60-70
• density: 0.95 g/cm³
• water absorption after 24 hours: <0.035%
• tensile strength:  <35 MPa
• Young´s modulus:  1000-1500 MPa
• elongation at break:>500 %
• Izod impact Strength Notched: No break
• flexural Strength: <35 MPa
• Vicat softening temperature: 125-130ºC
• melting temperature: 130-135ºC
• Coefficient of Friction COF: <0.3
• Heat Deflection Temperature HDT at 0.45MPa: >80ºC
• Heat Deflection Temperature HDT at 1.8MPa: >50ºC
• service temperature from -40ºC up to 80-90ºC (continuous)

Recommendations for SLS printing of HDPE:

• Recommended plastic or polymer powder SLS printers: SLS printer compatibility, any open mode plastic/ polymer powder SLS printer can be used
• Recommended printing, debinding and sintering process: use the std printing parameters of your equivalent polymer powder and follow 3Dresyns IFU for SLS printing
  
• reference printing settings*: energy density 2-40 J/cm2. Example: scan velocity of 1500-200 mm/s with 15-30 W CO2 laser (10.6 µm laser wavelength). Layer thickness <200 microns

*Note: the reported properties may vary depending of part design and manufacturing practices. It is the manufacturer’s responsibility to adjust the printing parameters and validate the suitability of the printed parts for the intended use. 3Dresyns. makes no guarantee of properties, expressed or implied, regarding the accuracy of these results to be obtained from the use thereof. Standards: Shore hardness (ISO868), density (ISO 1183), water Absorption after 24 hours (ISO 62), tensile strength (ISO 527-2), tensile modulus (ISO 527-2), elongation at break (ISO 527-2), Izod impact Strength Notched (ASTM D256 & ISO 180), flexural strength (ISO 178), flexural modulus (ISO 178), Vicat softening temperature (ISO 306/B50), melting temperature (ISO 11357), Coefficient of Friction COF-Static (ISO 8295), Heat Deflection Temperature HDT (ISO 75)