3Dresyn CG1 Clear Glass has these features and benefits:
- adjustable glass concentration to your printer specifications
- only sold as customised product due to high technical requirements of this high glass content material
-
very high resolution 3D printing for very high detail and resolution applications
- also suitable for moulding and UV curing
-
high print quality and speed with curing wavelengths up to 410 nm and higher upon request
-
controlled and reproducible process shrinkage
- excellent partial chemical debinding for faster thermal debinding with less risk of micro cracking
-
minimum expansion coefficient and wide temperature interval of debinding to prevent micro-fractures
-
very high resolution of 20 microns of final products
- reproducible shrinkage after sintering
-
printable by SLA DLP & LCD 3D printers ideally with heating
- increased durability of the resin tank
-
final sintering temperature 1300C
- final density of 3D printed clear glass: 2.2 g/cc
Starting point debinding process for 3Dresyn CG1 Glass:
- Insert flask in the preheated oven at 150-200ºC
- Ramp 1-2ºC/ minute up to 550ºC
- Hold at 550ºC for 30 minutes
- Ramp 1-2ºC/ minute up to sintering temperature of 1250-1300ºC
- Hold at sintering temperature for 120 minutes
- Ramp 1-2ºC/ minute down to 640ºC