3Dresyn Nylon-like has these features and benefits:
- ideal for the printing materials similar to Nylon / polyamide but without water absorption
- clear finishing unless your chosen color is added online
- tough and foldable , semirigid, pliable under pressure at low thickness <2 mm, with good memory until regains its original shape
- high relative impact and shattering resistance (Notched Izod <80 J/m)
- 100% biocompatible and food grade
- choose LV version for a relatively Low Viscosity for printing without heated printers or below 25ºC
- choose HV version for relatively High Viscosity version for printing with heated printers or above 25ºC, for overall improved durability and mechanical properties
- ultra pure and safe, non cytotoxic
- based on safe monomers
- hydrophobic, ultra low water absorption ULWA
- ultra tough with some flexibility below 2 mm
- Tensile strength >40 MPa
- Flexural strength >40 MPa and up to 80 MPa with the optimum printing and postcuring process*
- tough and flexible (Young modulus 1200-1700 MPa)
- ideal for engineering and biomedical systems
- high hardness, Shore hardness D70 range
- elongation <40%
- Glass transition temperature >35ºC
- LV version viscosity <10.000 cps at 25ºC
- very low shrinkage
- printable by SLA, DLP & LCD 3D printers
- increased durability of the resin tank
- organo-tin free
*IFU for 100% clarity & transparency (without any haziness or whitish finishing)
- print your 3D designs in any SLA, DLP and/or LCD printer following our printing instructions, which can be sent upon request by email: info@3dresyns.com
- after printing cut the supports and eliminate the uncured resin by gravity from the surface of the prints in the upside down position in an oven heated at 55-60ºC for 30 minutes
- postcure the dry prints in a normal light box for 30 minutes at T<50ºC
- clean parts by spraying IPA using a spray bottle to ensure that clean IPA is always used
- follow our more detailed Instructions for Use "IFU"